An investment powder which is safer than conventional powders comprising tricalcium phosphate, and being substantially or entirely free of free silica in the respiratory portion yet providing an overall expansion at 750°C of 1% or higher sufficient to prevent mould cracking during casting. A method of making a casting comprising forming a slurry by mixing a gypsum bonded investment powder with water, pouring the slurry into a stainless steel flask around a low melting point material model, allowing the slurry to set to define a mould, heating the mould to burn out the model and casting material into the mould wherein the stainless steel flask consists of a 400 series martensitic stainless steel.Cette invention concerne une poudre pour coulée qui est plus sûre que les poudres classiques comprenant du phosphate tricalcique, et est sensiblement ou entièrement exempte de silice libre dans la partie respiratoire tout en fournissant une expansion totale à 750 °C de 1 % ou plus suffisante pour empêcher la fissuration du moule pendant la coulée. Un procédé de fabrication d'une pièce coulée comprend les étapes consistant à : former une suspension par mélange d'une poudre pour coulée liée au gypse avec de l'eau, verser la suspension dans un ballon en acier inoxydable autour d'un modèle de matériau à bas point de fusion, laisser durcir la suspension pour définir un moule, chauffer le moule pour griller le modèle et couler le matériau dans le moule, le ballon en acier inoxydable étant constitué d'un acier inoxydable martensitique de série 400.