Федеральное государственное бюджетное учреждение "Национальный медицинский исследовательский радиологический центр" Министерства здравоохранения Российской Федерации (ФГБУ "НМИРЦ" Минздрава России)
发明人:
Комлев Владимир Сергеевич,Федотов Александр Юрьевич,Тетерина Анастасия Юрьевна,Зобков Юрий Валерьевич,Тютькова Юлия Борисовна,Баринов Сергей Миронович,Сергеева Наталья Сергеевна,Свиридова Ирина Конста
申请号：
RU2015144535
公开号：
RU2015144535A
申请日:
2015.10.16
申请国别(地区):
RU
年份:
2016
代理人:
摘要：
1. A method of producing a composite three-dimensional framework to replace the osteochondral defects, comprising preparing a flowable hydrogel comprising sodium alginate and calcium phosphate filler, applying the hydrogel to the platform, the formation of three-dimensional skeleton structure and then fixing, characterized in that the three-dimensional framework is formed by 3D printing injection layering hydrogel latching structure on the platform, cooled to a temperature of -5 ± 1 ° C to -30 ± 1 ° C during the deposition process, the flowable hydro spruce comprises by weight. %: 2. The method of claim. 1, characterized in that as a filler in a flowable hydrogel administered powders or granules of tricalcium phosphate, brushite, monetita, octacalcium phosphate, tetracalcium phosphate, hydroxyapatite, karbonatgidroksiapatita, ftorgidroksiapatita or other modifications, the particle size of the powder or granules vary from 20 to 500 microns, and said filler can be blended in any combination and in any amount between soboy.3. A method according to claim 1 and 2, characterized in that for producing three-dimensional framework with a porosity of 40 to 95% -. Of print completion frame is placed in a freezer and kept for 1 h at -50 ° C, then freeze-dried in processing chamber at a vacuum of 6 × 10atm., at a temperature of the condensing surface of -50 ° C for 10-12 h, dried skeleton crosslinked with 10% solution of calcium chloride in a shaker-incubator for 2 hours, then the resulting three-dimensional framework residue washed from salts, and again subjected to freeze-drying preservation of the structure.1. Способ получения композиционного трехмерного каркаса для замещения костно-хрящевых дефектов, включающий приготовление текучего гидрогеля, содержащего альгинат натрия и кальцийфосфатный наполнитель, нанесение гидрогеля на платформу, формирование трехмерного каркаса с последующей фиксацией структуры, отличающийся тем, что трехмерный каркас формируют методом 3D инъекционн