PROBLEM TO BE SOLVED: To provide a polyvinyl alcohol film for a seed tape, which is excellent in resolvability in water and soil, does not inhibit germination even in a small-sized seed particularly inferior in germinability by a swollen PVA film and is excellent in germinability and growth-promoting property.SOLUTION: There are provided: a polyvinyl alcohol film for a seed tape, which contains a polyvinyl alcohol-based resin (A) having viscosity of 4 wt.% aqueous solution at 20°C of 5-50 [mPa s] and a saponification degree of 70-85 mol% and/or a polyvinyl alcohol film which contains a polyvinyl alcohol-based resin (a1) having the viscosity of 4 wt.% aqueous solution at 20°C of 20-60 [mPa s] and the saponification degree of 70-85 mol%, and a polyvinyl alcohol-based resin (a2) having the viscosity of 2-20 [mPa s] and the saponification degree of 70-85 mol%, and has a difference of 5 [mPa s] or more of the above viscosity between the resins (a1) and (a2).COPYRIGHT: (C)2012,JPO&INPIT【課題】 水及び土中での溶解性に優れることはもちろん、特に発芽力が劣る小粒子の種子に対しても膨潤したPVA系フィルムにより発芽を阻害されず発芽性及び発育性に優れたシードテープ用ポリビニルアルコール系フィルムを提供。を提供すること。【解決手段】 20℃における4重量%水溶液粘度が5~50mPa・s、ケン化度が70~85モル%のポリビニルアルコール系樹脂(A)を含有してなるシードテープ用ポリビニルアルコール系フィルム、または、20℃における4重量%水溶液粘度が20~60mPa・s、ケン化度が70~85モル%のポリビニルアルコール系樹脂(a1)と20℃における4重量%水溶液粘度が2~20mPa・s、ケン化度が70~85モル%のポリビニルアルコール系樹脂(a2)を含有してなり、かつ、ポリビニルアルコール系樹脂(a1)とポリビニルアルコール系樹脂(a2)の4重量%水溶液粘度の差が5mPa・s以上であるシードテープ用ポリビニルアルコール系フィルム。【選択図】 なし