Disclosed is a ceramic body for dental prosthesis and a method for manufacturing the same, which can suppress variation in quality in a single dental prosthetic ceramic body accompanying an increase in diameter. The ceramic body for dental prosthesis is made of a ceramic material, is formed in a circular planar shape into a disk-like outer shape, and has a diameter of 50 mm or more. As a method for producing this dental prosthetic ceramic body, a ceramic material is prepared, the ceramic material is molded by press molding or a machine tool, and the theoretical density is obtained at a sintering temperature of −700 ° C. or higher and −100 ° C. or lower. This is a manufacturing method in which a ceramic material is pre-sintered to prepare a ceramic body for dental prosthesis having a circular planar shape and a disc-like outer shape having a diameter of 50 mm or more.直径の拡大に伴う、単一の歯科補綴用セラミックス体中での品質のバラツキが抑制可能になると共に、製造が容易な歯科補綴用セラミックス体とその製造方法を提供する。 歯科補綴用セラミックス体はセラミック材料から成り、円形の平面形状で円盤状の外形形状に成形され、５０ｍｍ以上の直径を有する。この歯科補綴用セラミックス体の製造方法としては、セラミック材料を用意し、そのセラミック材料をプレス成型又は工作機械により成形し、理論密度が得られる焼結温度から－７００℃以上且つ－１００℃以下でセラミック材料を仮焼結して、円形の平面形状で円盤状の外形形状に成形され５０ｍｍ以上の直径を有する歯科補綴用セラミックス体を用意する製造方法である。