The present disclosure relates to a method of forming a titania-coated inorganic particle comprising the steps of: (a) agitating a mixture of inorganic particle and organic solvent； (b) adding titania precursor, such as titanium alkoxide, dropwise into the mixture of step (a) under agitation； and (c) adding catalyst to the mixture of step (b) thereby converting said titania precursor to titania which then forms a coating on said inorganic particle； wherein steps (a) to (c) are performed at neutral pH and ambient temperature. In a preferred embodiment, the inorganic particle is a hollow glass bead and the catalyst is tap, distilled or deionized water. The titania coated particle may be used in reflective coatings for thermal insulation applications, antimicrobial coatings or UV-shielding for packing applications.La présente invention concerne un procédé de formation d'une particule inorganique enrobée de dioxyde de titane comprenant les étapes consistant à : (a) agiter un mélange de particules inorganiques et de solvant organique； (b) ajouter un précurseur de dioxyde de titane, tel qu'un alcoxyde de titane, goutte à goutte dans le mélange de l'étape (a) sous agitation； et (c) ajouter un catalyseur au mélange de l'étape (b), convertissant ainsi ledit précurseur de dioxyde de titane en dioxyde de titane qui forme ensuite un enrobage sur ladite particule inorganique； les étapes (a) à (c) étant effectuées à un pH neutre et à la température ambiante. Dans un mode de réalisation préféré, la particule inorganique est un cordon de verre creux et le catalyseur est du robinet, de l'eau distillée ou désionisée. La particule enrobée de dioxyde de titane peut être utilisée dans des enrobages réfléchissants pour des applications d'isolation thermique, des revêtements antimicrobiens ou un écran anti-UV pour des applications de conditionnement.