The present invention discloses different composition of magnesium added fluorophosphate glasses prepared using melt-quench method. The physico-chemical and bio conversion of magnesium added fluorophosphate glasses were accessed using density measurements, ultrasonic measurements to determine elastic moduli, XRD pattern, FTIR spectra, pH variations during 21 days of in vitro studies in SBF solution, SEM images, EDS spectra and XPS spectrograph. Bioconversion was also accessed by in vivo studies of implantation of the optimized glass into animal bone for 10 weeks followed by SEM images, EDS spectra and CLSM images. The result obtained before, after in vitro and in vivo studies are discussed in terms of structure, stability, mechanical properties, bone bonding ability and bioconversion of the prepared glass samples. The sample MgFP5 is found to be more ideal and better than other samples for future clinical use.Linvention concerne différentes compositions de verres de fluorophosphate contenant du magnésium préparées par un procédé de fusion-trempe. La conversion physico-chimique et biologique des verres de fluorophosphate contenant du magnésium est étudiée par des mesures de densité, des mesures ultrasonores pour déterminer les modules élastiques, les formes par diffraction des rayons X, les spectres FTIR, le spectrographe XPS, les variations de pH pendant 21 jours détudes in vitro en solution SBF, images SEM et spectres EDS. La bioconversion est également étudiée par des analyses in vivo dimplantation du verre optimisé dans un os animal pendant 10 semaines avant images SEM, spectres EDS et images CLSM. Le résultat obtenu avant et après les études in vitro et in vivo est analysé en termes de structure, de stabilité, de propriétés mécaniques, de capacité à se lier à los et de bioconversion des échantillons de verre préparés. Léchantillon de MgFp5 savère idéal et meilleur que les autres échantillons pour une utilisation clinique ultérieure.