The present invention relates to a method for manufacturing a dental zirconia implant member and a dental zirconia implant member using the same, a method that can easily produce an implant member having aesthetically superior and high strength and toughness by injection molding a zirconia material and It relates to a dental zirconia implant member using the same. The method for producing a dental zirconia implant member of the present invention is a molding step of injection molding by mixing a zirconia powder and a binder, and heated to 450 ℃ by heating for 35 to 45 hours to remove the binder contained in the molded body formed in the molding step After the heat treatment step of cooling and cooling the molded body heat-treated in the heat treatment step for 22 to 30 hours, the temperature is raised to 1400 ℃, the temperature is lowered to 1000 ℃ and the sintering step, and the molded product sintered in the sintering step into the mold And then a post-treatment step of densifying the tissue by applying heat under isostatic pressure.본 발명은 치과용 지르코니아 임플란트 부재의 제조방법 및 이를 이용한 치과용 지르코니아 임플란트 부재에 관한 것으로서, 지르코니아 소재를 사출성형하여 심미적으로 우수하고 높은 강도와 인성을 가진 임플란트 부재를 용이하게 제조할 수 있는 방법 및 이를 이용한 치과용 지르코니아 임플란트 부재에 관한 것이다. 본 발명의 치과용 지르코니아 임플란트 부재의 제조방법은 지르코니아 분말과 바인더를 혼합하여 사출성형하는 성형단계와, 성형단계에서 형성된 성형체 중에 함유된 바인더를 제거하기 위해 35 내지 45시간 동안 가열하여 450℃까지 승온시킨 후 냉각시키는 열처리단계와, 열처리단계에서 열처리된 성형체를 22 내지 30시간 동안 가열하여 1400℃까지 승온시킨 후 1000℃까지 강온시킨 다음 냉각시키는 소결단계와, 소결단계에서 소결된 성형체를 몰드에 투입한 후 등압상태에서 열을 가하여 조직을 치밀화시키는 후처리단계를 포함한다.