The present invention relates to a filter for a blood filter, and to a method for manufacturing the same. The filter for a blood filter having the weight of 21-22 g/5m^2, thickness of 280-310 &mu；m, pore size of 16-18 &mu；m, porosity of 79-82%, and tensile strength of 290-310 MPa is formed by melt-blowing peroxide-free type polypropylene, which is a raw material, into a composite electrospun fiber through a spinning nozzle of a conventional melt blown composite spinning, thereby satisfying the high leukocyte removal rate and erythrocyte removal rate, while having excellent plasma separation efficiency, and having excellent performance as a blood filter by reducing platelet adhesion rate remaining on the filter.본 발명은 혈액 필터용 여재 및 그 제조 방법에 관한 것으로서 과산화물이 들어있지 않은 폴리프로필렌(peroxide-free type polypropylene)을 원료로 하여 통상의 멜트블로운 복합방사의 방사노즐을 통해 복합방사섬유로 멜트블로운하여, 중량은 21~22g/5㎡이고, 두께는 280~310㎛이며, 공극의 크기는 16~18㎛이고, 공극률은 79~82%로서 290~310MPa의 인장강도를 가지는 혈액 필터용 여재를 구성함으로써 높은 백혈구 제거율 및 적혈구 회수율을 만족함과 동시에 우수한 혈장분리효율을 가지면서도 여재에 잔존하는 혈소판 점착률을 저하시켜 혈액 필터로서 우수한 성능을 발휘하는 효과가 있다.