The present disclosure relates to polymeric siloxane coated zinc oxide powders having a mean particle size number distribution (D50) ranging from about 300 nm to about 600 nm and their use in sunscreen compositions. The relatively high surface area (in relation to particles of <；100 nm) avoids agglomeration resulting in ease of formulation and high dispersal of the particles which tends toward less light scatter and hence better transparency in formulations. Furthermore, the combination of the particular particle size number distribution (D50) of zinc oxide ranging as above with bis(resorcinyl)triazine UV absorbers shows unexpected increased UV-A absorbance (320 to 400 nm) in comparison to the zinc oxide and bis resorcinyl triazine UV absorbers on their own at the same concentration.본 개시는 약 300 nm 내지 약 600 nm 범위의 평균 입자 크기 수 분포 (D50)를 갖는, 중합체 실록산 코팅된 산화아연 분말, 및 선스크린 조성물에서의 그의 용도에 관한 것이다. 상대적으로 큰 표면적 (<； 100 nm의 입자 대비)은 응집을 방지함으로써 제제화의 용이성 및 고도의 입자 분산성을 초래하는데, 이는 더 적은 광 산란 및 그에 따른 제제에서의 더 우수한 투명도로 이어진다. 또한, 상기와 같은 범위의 특정 입자 크기 수 분포 (D50)의 산화아연과 비스(레조르시닐)트리아진 UV 흡수제와의 조합은 동일 농도에서의 산화아연 및 비스 레조르시닐 트리아진 UV 흡수제 자체 단독과 비교할 때 예상치 못한 증가된 UV-A 흡광도 (320 내지 400 nm)를 나타낸다.