The present invention proposes a method for producing a polygonal zinc oxide platelet having a median specific surface area of greater than 25 square meters per gram, in controlled size and shape, the method comprising the following steps: release free protons to release Zn ions In a medium suitable for substituting, preparing a medium containing Zn or a compound thereof at a concentration in the range of 1.55 to 7.75 mol Zn / L, thereby forming a complex structure comprising Zn； Stirring the medium in the vessel at a temperature in the range of 50 ° C to 320 ° C for up to 10 hours to obtain a suspension； Filtering the suspension to obtain a filtrate comprising solid particles； After drying the filtrate, calcining the dried filtrate； Here, the stirring step is performed with one or more semi-current type impellers so that the Reynolds number in the container is 2500 or more and less than 10000. The present invention further proposes products comprising such platelets.본 발명은 제어된 크기 및 형태로, 중앙 비표면적이 그램 당 25 제곱 미터 초과인 다각형 산화 아연 소판을 제조하는 방법을 제안하며, 상기 방법은 다음의 단계를 포함한다: 자유 양성자를 방출하여 Zn 이온을 치환하기에 적합한 매질에서, Zn 또는 이의 화합물을 1.55 내지 7.75 몰 Zn/L 범위 내의 농도로 포함하는 매질을 제조하여, Zn을 포함하는 복합 구조체를 형성하는 단계； 용기 내의 매질을 50 ℃ 내지 320 ℃의 범위 내의 온도에서 최대 10 시간 동안 교반하여, 현탁액을 획득하는 단계； 현탁액을 여과하여, 고체 입자를 포함하는 여과액을 획득하는 단계； 여과액을 건조한 후, 건조된 여과액을 소성시키는 단계； 여기서 교반 단계는 용기 내 레이놀즈 수(Reynolds' number)가 2500 이상 10000 미만이 되도록 하나 이상의 반경류형 임펠러로 수행된다. 본 발명은 추가로 이러한 소판을 포함하는 제품을 제안한다.