Guide wire devices fabricated from a linear pseudo-elastic Ni-Ti alloy and methods for their manufacture. The Ni-Ti alloy that includes nickel, titanium, and about 3 atomic % (at%) to about 30 at% niobium (Nb). Cold working the Ni-Ti alloy stabilizes the alloys martensitic phase and yields a linear pseudo-elastic microstructure where reversion to the austenite phase is retarded or altogether blocked. The martensitic phase of cold worked, linear pseudo-elastic Ni-Ti-Nb alloy has an elastic modulus that is considerably higher than the comparable cold worked, linear pseudoelastic binary Ni-Ti alloy. This yields a guide wire device that has better torque response and steerability as compared to cold worked, linear pseudoelastic binary Ni-Ti alloy or superelastic binary Ni-Ti alloy.Linvention concerne des dispositifs de fil-guide fabriqués à partir dun alliage Ni-Ti pseudo-élastique linéaire et leurs procédés de fabrication. Lalliage Ni-Ti qui comprend du nickel, du titane et environ 3 % atomique (% at) à environ 30 % at de niobium (Nb). Le travail à froid de lalliage Ni-Ti stabilise la phase martensitique de lalliage et fournit une microstructure pseudo-élastique linéaire où linversion de la phase austénite est retardée ou entièrement bloquée. La phase martensitique de lalliage Ni-Ti-Nb pseudo-élastique linéaire, travaillé à froid a un module élastique qui est considérablement supérieur à lalliage Ni-Ti binaire pseudo-élastique linéaire, travaillé à froid comparable. Ceci fournit un dispositif de fil-guide qui a une meilleure réponse de couple et une meilleure capacité de direction par comparaison à lalliage Ni-Ti binaire pseudo-élastique linéaire, travaillé à froid ou un alliage Ni-Ti binaire super élastique.