The purpose of the present invention is to provide a powdered gyro-light-type calcium silicate having a comparatively large particle diameter and also having high oil absorbency and high particle strength. This powdered gyro-light-type calcium silicate is characterized by: (1) having an oil absorbency of at least 2.8 mL/g (2) having an average particle diameter of at least 40 µm and (3) the change in the average particle diameter between before processing and after processing being no more than 15%, said processing being the insertion of the gyro-light-type calcium silicate to a laser diffraction particle size distribution meter such that the DV value becomes 0.1-0.6, and circulating same for 5 minutes at a flow rate of 32.5 mL/sec.La présente invention vise à fournir un silicate de calcium en poudre de type lumière gyro, ayant une granulométrie relativement grosse et ayant aussi une absorption élevée des huiles et une grande résistance mécanique des particules. Ce silicate de calcium en poudre de type lumière gyro est caractérisé en ce que : (1) il a une absorption des huiles dau moins 2,8 ml/g (2) il a une granulométrie moyenne dau moins 40 µm et (3) le changement de la granulométrie moyenne entre avant le traitement et après le traitement nest pas supérieur à 15 %, ledit traitement étant linsertion du silicate de calcium de type lumière gyro dans un compteur à diffraction laser de la distribution granulométrique, de telle sorte que la valeur DV devienne 0,1 à 0,6, et sa circulation pendant 5 minutes à un débit de 32,5 ml/s.本発明は、比較的大きな粒子径を有しながらも、高い吸油量と高い粒子強度を兼ね備えた粉末状ジャイロライト型ケイ酸カルシウムの提供を目的・課題とする。 そして、本発明の粉末状ジャイロライト型ケイ酸カルシウムは、(1)吸油量が2.8mL/g以上であり、(2)平均粒子径が40μm以上であり、(3)当該ジャイロライト型ケイ酸カルシウムをレーザー回折式粒度分布計にDV値0.1~0.6になるように投入し、流量32.5mL/秒で5分間循環させる処理において、処理前の平均粒子径に対する処理後の平均粒子径の変化率が15%以下であることを特徴とする。