Ceramic particles dispersed in a single crystal primary particles in a solvent, and a manufacturing method thereof, the invention is intended to be as well as the use of such particles. In the production of the (ceramic particles) group, one embodiment of the production method according to the present invention, sintered state of being interposed calcium between the primary particles of hydroxyapatite (HAp) sintered particles of hydroxyapatite (HAp) After then, the step of removing after dissolving in water of calcium carbonate. Hydroxyapatite obtained by the production method (HAp) sintered particles, the particle diameter (12% coefficient of variation) and uniform particles and particle size, in the nanometer-sized particles of about 70 to about 120nm Yes, it was intended that the 96% is distributed as a single crystal primary particles in a solvent further.本発明は、溶媒中で単結晶一次粒子で分散するセラミック粒子群、およびその製造方法、並びにその粒子群の用途を提供することを目的としている。本発明にかかる製造方法の一態様は、ハイドロキシアパタイト(HAp)の焼結体粒子(セラミック粒子)群の製造に際し、ハイドロキシアパタイト(HAp)の一次粒子間に炭酸カルシウムを介在させた状態で焼結させた後、炭酸カルシウムを水で溶解させて除去する工程を含む。当該製造方法によって得られたハイドロキシアパタイト(HAp)焼結体粒子群は、粒子径が約70~約120nmのナノメートルサイズ粒子で、かつその粒子径が均一な粒子群(変動係数12%)であり、さらに溶媒中でその96%が単結晶一次粒子として分散するものであった。