PURPOSE: A manufacturing method of porous CeO2 composite powder is provided to have micron-size which can limit skin penetration by combining nano-powder, SiO2 nano-powder, and organic template and manufacturing porous CeO2-SiO2 composite powder. CONSTITUTION: A manufacturing method of porous CeO2 composite powder comprises next steps: manufacturing colloid solution by mixing CeO2, SiO2, and organic template； spraying the colloidal solution in a microdroplet form； obtaining CeO2-SiO2- organic template type compound powder by desiccating the colloidal droplet； and obtaining porous CeO2-SiO2 compound powder by eliminating the organic template from the compound powder. A content amount of the mixed nano-powder of CeO2 and SiO2 in the colloidal solution is 1-10wt%. CeO2 content amount in the mixture of SiO2 and CeO2 is 5- 50wt%. A weight of the organic template is 0.5-6 times of the mixture of CeO2 and SiO2. The CeO2 is manufactured by using a flame spray pyrolysis.본 발명은 마이크론 크기의 다공성 CeO2-SiO2 복합 분말의 제조방법, 상기 제조방법에 따라 제조된 수 ~ 수십 마이크론크기를 갖는 다공성 CeO2-SiO2 복합 분말 및 상기 복합 분말을 포함하는 자외선 차단용 화장료 조성물에 관한 것이다. 본 발명의 제조방법에 따라 제조된 다공성 CeO2-SiO2복합분말은 피부 침투를 제한시킬 수 있는 마이크론 크기를 가지며, 뛰어난 자외선 차단율 및 가시광선에 대한 투명도를 유지하여 백탁 효과를 일으키지 않는 장점이 있으므로, 기존 상용분말을 대체할 수 있는 자외선 차단제 원료로 사용될 수 있다.