Electronic pulsed bombardment for biodegradable magnesium alloy prostheses. This innovative method improves the viability of medical implants, dental implants and products for osteosynthesis. The alloys involved are mainly magnesium alloys that are poorly resistant to corrosion in vivo. This method offers an innovative surface treatment, used selectively or not. This method controls and adjusts the corrosion rate of magnesium alloy implants. The treatment itself is called pulsed electronic bombardment (LEHCPEB / Low Energy High Current Pulsed Electron Beam). In this sense, Figure (1) shows as an example a hip prosthesis component being processed. The intensity of the treatment is adjusted so as to have areas more or less resistant to corrosion. The bone will develop preferentially in the untreated zones, dissolved first in the body. Bombardement électronique puisé pour prothèses biodégradable en alliage de magnésium. Cette méthode innovante améliore la viabilité des implants médicaux, dentaires et produits pour l'ostéosynthèse. Les alliages concernés sont principalement les alliages de magnésium qui résistent mal à la corrosion in vivo. Cette méthode propose un traitement de surface innovant, utilisé de manière sélective ou non. Cette méthode permet de contrôler et d'adjuster la vitesse de corrosion des implants en alliage de magnesium. Le traitement ,en lui-même , s'appelle le bombardement électronique pulsé (LEHCPEB / Low Energy High Current Pulsed Electron Beam). Dans ce sens, la figure (1) présente commme exemple un élément de prothèse de hanche en cours de traitement. L'intensité du traitement est ajustée de façon à avoir des zones plus ou moins résistante à la corrosion. L'os se développera préférentiellement dans les zones non traitées, dissoutes en premier dans l'organisme.