The present invention is a multiphase polymer comprising 45% to 95% by weight of a first polymer P1 and 5% to 55% by weight of a second polymer P2, wherein the polymers P1 and P2 have a separate composition. -The polymer P1 is at least one anionic monomer (a) having a polymerizable vinyl group, at least one nonionic hydrophobic monomer (b) having a polymerizable vinyl group, at least one crosslinkable monomer ( c) and obtained by polymerization from a mixture of monomers comprising a polymerizable vinyl group and at least one associative monomer (d) having a hydrophobic hydrocarbon chain, wherein the polymer P2 has at least a polymerizable vinyl group One anionic monomer (a ′), at least one nonionic hydrophobic monomer (b ′) having a polymerizable vinyl group Obtained by polymerization of a mixture of monomers comprising at least one crosslinking monomer (c '), it relates to a multiphase polymer. The present invention also relates to a process for the preparation of these polymers, aqueous compositions containing them and their use as thickeners and suspending agents.本発明は、４５重量％から９５重量％の第１のポリマーＰ１および５重量％から５５重量％の第２のポリマーＰ２を含む多相ポリマーであって、前記ポリマーＰ１およびＰ２は別個の組成であり、 －前記ポリマーＰ１が、重合性ビニル基を有する少なくとも１つのアニオン性モノマー（ａ）、重合性ビニル基を有する少なくとも１つの非イオン性疎水性モノマー（ｂ）、少なくとも１つの架橋性モノマー（ｃ）ならびに重合性ビニル基および疎水性炭化水素鎖を有する少なくとも１つの会合性モノマー（ｄ）を含むモノマーの混合物からの重合によって得られ、 －前記ポリマーＰ２が、－重合性ビニル基を有する少なくとも１つのアニオン性モノマー（ａ’）、－重合性ビニル基を有する少なくとも１つの非イオン性疎水性モノマー（ｂ’）、少なくとも１つの架橋性モノマー（ｃ’）を含むモノマーの混合物からの重合によって得られる、多相ポリマーに関する。 本発明は、これらのポリマーの調製方法、これを含む水性組成物ならびに増粘剤および懸濁化剤としてのこれの使用にも関する。