The present invention relates to a mask pack material having a microporous polyurethane foam structure. More particularly, the present invention relates to a polyurethane mask pack material which improves the pore uniformity of a foam by using a prepolymer, And a manufacturing method thereof. (A) adding isocyanate to a mixed solution containing a polyol, a diol and an antioxidant to obtain a polyurethane prepolymer having a viscosity of 6,000 to 12,000 cps at 25 ° C at 60 ° C； (b) adding 50 to 150 parts by weight of the foamed composition to 100 parts by weight of the polyurethane prepolymer obtained above, and mixing at high speed to prepare a foamed mixture； (c) applying the foamed mixed solution prepared in (b) above onto a release paper to obtain a sheet-like microporous polyurethane foam layer； (d) laminating a breathable and waterproof polyurethane film on top of the polyurethane foam layer obtained in (c)； And (e) laminating a perforated polyurethane film at the bottom of the polyurethane foam layer obtained in (c) above. The polyurethane mask pack material obtained according to the present invention is superior in physical properties and functionality of the pack material such as density, tensile strength, elongation, etc., as compared with conventional polyurethane pack materials.본 발명은 미세다공성 폴리우레탄 폼 구조의 마스크 팩재에 관한 것으로, 특히 프리폴리머를 이용하여 제조공정이 개선되면서도 폼의 기공 균일성이 향상되고 사용감이 우수하며 curl 현상이 발생되지 않는 폴리우레탄 마스크 팩재 및 그의 제조방법에 관한 것이다. 본 발명에서는, (a) 폴리올과 다이올 및 산화방지제가 포함된 혼합용액에 이소시아네이트(Isocyanate)를 투입하여 60℃에서 합성하여 25℃에서 점도 6,000~12,000cps의 폴리우레탄 프리폴리머를 얻는 단계； (b) 상기에서 얻은 폴리우레탄 프리폴리머 100 중량부에, 발포조성물을 50~150 중량부로 가하고 고속으로 혼합하여 발포 혼합액을 만드는 단계； (c) 상기 (b)에서 만든 발포 혼합액을 이형지 위에 도포하여 시트상의 미세다공성 폴리우레탄 폼층을 얻는 단계； (d) 상기 (c)에서 얻은 폴리우레탄 폼층의 상부에 투습방수성의 폴리우레탄 필름을 합지하는 단계； 및 (e) 상기 (c)에서 얻은 폴리우레탄 폼층의 하부에 천공된 폴리우레탄 필름을 합지하는 단계；를 포함하는 폴리우레탄 마스크 팩재의 제조방법이 제공된다. 본 발명에 따라 얻어진 폴리우레탄 마스크 팩재는, 기존 폴리우레탄 팩재에 비해 기공이 균일하고 사용감이 좋으며, 밀도, 인장강도, 신장율 등 팩재의 물성과 기능성이 우수하다.