the present invention, non-ionic and a low substituted hydroxypropylcellulose stability excellent improve the moldability and flowability of, and improve the collapse resistance, of the dose in the mouth. More specifically, the present invention is to from the diffraction intensity measured by wide-angle X-ray diffraction method, the degree of crystallinity is calculated by Equation (1) not more than 60%, a hydroxy propoxy substitution is from 5 to 9 mass%, the aspect ratio less than 2.5 provides low-substituted hydroxypropyl cellulose. & lt Equation 1 & gt Crystallinity (%) = (Ia-Ic) / Ic 100 (In the formula (1), and Ic is the diffraction angle 2 = 22.5 diffraction intensity in Fig, Ia is being diffracted intensity of diffraction at each 2 = 18.5 degree)본 발명은, 비이온성이며 안정성이 우수한 저치환도 히드록시프로필셀룰로오스의 성형성과 유동성을 개선하고, 붕괴성, 구강내에서의 복용성을 개선한다.구체적으로 본 발명은, 광각 X선 회절법에 의해 측정된 회절 강도로부터 하기 수학식 1에 의해 산출되는 결정화도가 60 % 이하이고, 히드록시프로폭시기 치환도가 5 내지 9 질량%이며, 종횡비가 2.5 미만인 저치환도 히드록시프로필셀룰로오스를 제공한다.<수학식 1>결정화도(%)={(Ic-Ia)/Ic}×100(상기 수학식 1 중, Ic는 회절각 2θ=22.5도에서의 회절 강도이고, Ia는 회절각 2θ=18.5도에서의 회절 강도임)