A glove with thickness from about 0.05 mm to 0.3 mm having stress retention greater than 50% at 100% stretch, tensile stress at break greater than 17 Mpa and elongation at break greater than 550% is made from a carboxylated acrylonitrile butadiene elastomer comprising 20-30% acrylonitrile, 63-77% butadiene and 3-7% carboxylic acid dry weight of elastomer and crosslinked by 1.0 - 4.0 phr aluminum ion compound.本發明揭露一種具高強度保留的丁腈橡膠手套,其具有0.05-0.3 mm的厚度,100%伸展時的強度保留率大於50%,破裂抗拉強度大於17Mpa,破裂延伸率大於550%的特性。本發明手套是由一種羧化丙烯腈丁二烯彈性體所製造,其中該羧化丙烯腈丁二烯彈性體包含:乾重20-30%丙烯腈、63-77%丁二烯、及3-7%羧酸,且與1.0-4.0 phr的鋁離子化合物交聯。無