The invention relates to a copper alloy, composed of (in wt %): 51.8 to 84.0% Cu, 15.5 to 36.0% Zn, 0.35 to 3.0% Sn, 0.12 to 1.5% Fe, 0.02 to 1.0% P, optionally also 0.1 to 2.0% Al, optionally also 0.05 to 0.7% Si, optionally also 0.05 to 2.0% Ni, optionally also respectively 0.1 to 1.0% Mn, Co, optionally also respectively 0.01 to 1.0% As, Sb, and unavoidable contaminants, wherein more than 95% of the structure consist of α-mixed crystal, in which at least iron phosphides and/or iron are embedded as deposition particles, which can be used for metallic articles in breeding organisms living in seawater.<；p>；LA INVENCIÓ；N SE REFIERE AL USO DE UNA ALEACIÓ；N DE COBRE, COMPUESTA POR (EN % EN PESO): ； 51,8 A 84,0% DE CU, 15,5 A 36,0 % DE ZN, 0,35 A 3,9% DE SN, 0,12 A 1,5% DE FE, 0,02 A 1,0% DE P, A ELECCIÓ；N TAMBIÉ；N 0,1 A 2,0% DE AL A ELECCIÓ；N TAMBIÉ；N 0,05 A 0,7% DE SI A ELECCIÓ；N TAMBIÉ；N 0,05 A 2,0% DE NI A ELECCIÓ；N EN CADA CASO TAMBIÉ；N 0,01 A 1,0% DE MN, CO A ELECCIÓ；N CADA CASO TAMBIÉ；N 0,01 A 1,0% DE AS, SB E IMPUREZAS INEVITABLES, EN DONDE: LA ESTRUCTURA ESTA COMPUESTA EN MAS DE 95% POR CRISTAL MIXO A, EN EL CUAL SE ENCUENTRAN INCORPORADOS POR LO MENOS FOSFUROS DE HIERRO Y/O HIERRO COMO PARTÍ；CULAS DE DEPOSICIÓ；N, PARA OBJETOS METALICOS EN LA CRIA DE ORGANISMOS QUE VIVEN EN EL AGUA DE MAR.<；/p>；