Provided are: a plastic molded product comprising copper-based compound microparticles which is relatively cheap, can be easily processed, is economical and has production efficiency and a preparation method therefor. The molded product comprises a thermoplastic resin in which copper-based nanoparticles having an average diameter of 20-500 nm are dispersed, wherein the copper-based nanoparticles are represented by chemical structure CuxMy (wherein M is any one selected from groups 15-17 elements in the periodic table, and x/y = 0.8-1.2), and are generated from copper sulfate and any one selected from a sulfate, a fluoride and a chloride in a molar ratio of 1:1 in an aqueous solution at 50-80℃.Linvention concerne un produit moulé en plastique comprenant des microparticules en composé à base de cuivre qui est relativement bon marché, peut être traité facilement, est économique et présente une efficacité de production et son procédé de préparation. Le produit moulé comprend une résine thermoplastique dans laquelle des nanoparticules à base de cuivre présentant un diamètre moyen de 20-500 nm sont dispersées, les nanoparticules à base de cuivre étant représentées par la structure chimique CuxMy (dans laquelle M est lun quelconque élément choisi dans les groupes des éléments 15-17 du tableau périodique et x/y = 0,8-1,2), et générées à partir de sulfate de cuivre et lun quelconque composé choisi parmi un sulfate, un fluorure et un chlorure dans un rapport molaire de 1:1 dans une solution aqueuse à 50-80℃.가격이 상대적으로 저렴하고 가공이 용이하며, 경제성 및 생산 효율성을 갖춘 구리계 화합물 미립자를 포함하는 플라스틱 성형품 및 그 제조방법을 제시한다. 그 성형품 및 방법은 화학구조는 CuxMy(M은 주기율표에서 15족 내지 17족 중에서 선택된 어느 하나, x/y=0.8∼1.2)이고, 수용액상에서 황산구리와 황화염, 불소화염, 염화염 중에서 선택된 어느 하나의 염을 1:1의 몰비로 50~80℃의 온도 범위에서 생성된 평균입경이 20~500nm인 구리계 나노입자가 분산된 열가소성 수지로 이루어진다.