There is provided a breathable film formed from a thermoplastic composition comprising a strong, reproducible polyester and having a voided structure. To achieve such a structure, a thermoplastic composition comprising a renewable polyester and a polymer curing additive is extruded onto the surface to separate the curing additive in a continuous matrix of renewable polyester. Form a precursor film that can be dispersed as physical domains. The precursor film is then stretched or stretched (ie, “cold stretched”) at a temperature below the glass transition temperature of the polyester. While not intending to be limited by theory, the inventors have shown that the original deformation force and tensile strain of the stretching process occur in a polyester matrix that is reproducible in these regions located adjacent to the separated domains. To cause peeling. This results in a network of voids located adjacent to the separated domains.強固な再生可能なポリエステルを含み、かつ空隙のある構造を有する熱可塑性組成物から形成される通気性フィルムが提供される。このような構造を達成するために、再生可能なポリエステルおよび重合体硬化添加物を含む熱可塑性組成物を表面上に押出加工して、硬化添加物が再生可能なポリエステルの連続マトリックス内の分離した物理的なドメインとして分散することができる前駆フィルムを形成する。その後、前駆フィルムをポリエステルのガラスの転移温度以下の温度にて伸ばし、または延伸する（すなわち、「冷延伸する」）。理論によって制限されることは意図しないが、本発明者らは、延伸工程の原変形力および引張り歪みが分離したドメインに隣接して位置したこれらの領域にて再生可能なポリエステルマトリックスに生じさせるように剥離を引き起こすと考える。これは、分離したドメインに隣接して位置した空隙のネットワークを生じる。