PROBLEM TO BE SOLVED: To provide a fiber material excellent in processability for compounding cellulose nanofibers and a method for producing the same. A method for producing a fiber material includes a step of obtaining a CNF dispersion and a drying step. In the step of obtaining a CNF dispersion, an aqueous dispersion of cellulose nanofibers in which cellulose nanofibers are dispersed in an aqueous solvent, a cationic surfactant, a polyhydric alcohol and polyvinyl alcohol are mixed. In the drying step, the aqueous solvent is removed from the CNF dispersion obtained in the step of obtaining the CNF dispersion to obtain a fiber material. The mass ratio of the cationic surfactant to the cellulose nanofibers in the CNF dispersion is 0.1 to 2.0 times. The mass ratio of the polyhydric alcohol to the cellulose nanofibers in the CNF dispersion is 2 to 20 times. The mass ratio of polyvinyl alcohol to cellulose nanofibers in the CNF dispersion is 0.02 to 10.0 times. [Selection diagram] Figure 1【課題】本発明は、セルロースナノファイバーを複合化するための加工性に優れた繊維材料及びその製造方法を提供する。【解決手段】繊維材料の製造方法は、ＣＮＦ分散液を得る工程と、乾燥工程と、を含む。ＣＮＦ分散液を得る工程は、水系溶媒にセルロースナノファイバーが分散したセルロースナノファイバー水分散液とカチオン界面活性剤と多価アルコールとポリビニルアルコールとを混合する。乾燥工程は、ＣＮＦ分散液を得る工程で得られたＣＮＦ分散液から水系溶媒を除去して繊維材料を得る。ＣＮＦ分散液におけるセルロースナノファイバーに対するカチオン界面活性剤の質量比が０．１倍～２．０倍である。ＣＮＦ分散液におけるセルロースナノファイバーに対する多価アルコールの質量比が２倍～２０倍である。ＣＮＦ分散液におけるセルロースナノファイバーに対するポリビニルアルコールの質量比が０．０２倍～１０．０倍である。【選択図】図１