PROBLEM TO BE SOLVED: To provide a novel method for manufacturing a material for osteoanagenesis containing calcium phosphate particles in a biodegradable fiber consisting of PLGA by using electrospinning, and a novel material for osteoanagenesis manufactured by the method.SOLUTION: A PLGA resin is heated in a kneader, and softened to have viscosity of the resin of 102 to 107 Pa s, a powder of calcium phosphate fine particles is input and the powder and the softened PLGA resin are mixed, thermal and mechanical energy are applied to the mixture and mixed to prepare a composite in which fine particles of the calcium phosphate is dispersed in the PLGA resin, a spinning solution in which the PLGA resin is completely dissolved by a solvent and the calcium phosphate fine particles are dispersed without aggregation in a solution in which the PLGA resin is dissolved is prepared, and a biodegradable fiber in which the calcium phosphate fine particles are dispersed in the biodegradable fiber almost uniformly by electrospinning using the spinning solution is manufactured.SELECTED DRAWING: Figure 4(1)COPYRIGHT: (C)2018,JPO&INPIT【課題】PLGAからなる生分解性繊維にリン酸カルシウム粒子を含有させた骨再生用材料をエレクトロスピニングを用いて製造するための新たな方法、およびその方法で製造された新たな骨再生用材料の提供。【解決手段】PLGA樹脂をニーダー中で加熱して、樹脂の粘度が102~107Pa・sになるまで軟化させ、リン酸カルシウム微粒子の粉体を投入することによって、粉体を軟化したPLGA樹脂と混合し、前記混合物に対して熱的かつ機械的エネルギーをかけて混練し、リン酸カルシウムの微粒子がPLGA樹脂中に分散した複合体を作製し、PLGA樹脂が溶剤によって完全に溶解され、かつリン酸カルシウム微粒子がPLGA樹脂が溶解された溶液中で凝集することなく分散した紡糸溶液を作製し、当該紡糸溶液を用いてエレクトロスピニングすることによって、リン酸カルシウム微粒子が生分解性繊維中に略均一に分散している生分解性繊維を製造する。【選択図】図4(1)