FIELD: chemistry.SUBSTANCE: invention relates to carbon materials. Described is a method of producing porous carbon material from silicon-containing plant material. The method involves carbonising plant material by temperature treatment, treating with acid or alkali, followed by activation. The porous carbon material has nitrogen BET specific surface area of at least 130 m2/g, mesopore and micropore volume of at least 0.1 cm3/g, measured by BJH method and MP method and containing more mesopores smaller than 20 nm than mesopores having size of at least 20 nm. The obtained material is used, for example, as an adsorbent, an adsorbent for oral administration, a medical adsorbent, a creatinine adsorbent, a cap for blood purification columns, a water treatment adsorbent, a mask, an adsorbent sheet, a medicine carrier and a carbon-polymer complex.EFFECT: invention enables to obtain material with a wide range of applications.10 cl, 10 dwg, 12 tbl, 8 exИзобретение относится к углеродным материалам. Описан способ получения пористого углеродного материала из содержащего кремний материала растительного происхождения. Способ включает карбонизацию материала растительного происхождения путем температурной обработки, обработку кислотой или щелочью с последующей активацией. Пористый углеродный материал имеет величину удельной площади поверхности, по меньшей мере, 130 м2/г, измеряемую способом BET по азоту, объем мезопор и микропор, по меньшей мере, 0,1 см3/г, измеренный способом BJH и способом МР и содержащий больше мезопор, имеющих размер меньше чем 20 нм, чем мезопор, имеющих размер по меньшей мере 20 нм. Полученный материал используют, например, в качестве адсорбента, адсорбента перорального введения, медецинского адсорбента, адсорбента для поглощения креатинина, насадки для колонн очистки крови, водоочищающего адсорбента, маски, адсорбирующего листа, носителя для лекарства и углерод-полимерного комплекса. Изобретение обеспечивает получения материала широкого спектра применения