The present invention provides a dental mill blank having reduced cracks and that excels in mechanical strength and aesthetic quality. The present invention relates to a dental mill blank comprising an inorganic filler and a polymer, and having a porosity of 25 to 35 volume % after 2-hour ashing at 600° C. In the dental mill blank, the inorganic filler preferably comprises an inorganic filler (A) and an inorganic filler (B), and the dental mill blank preferably satisfies the following formulae (I) and (II),0.12≤；a≤；0.70 ； ；(I)3≤；b/a ； ；(II),where a is an average primary particle diameter of the inorganic filler (A) in micrometers, and b is an average primary particle diameter of the inorganic filler (B) in micrometers. Preferably, the inorganic filler (A) and the inorganic filler (B) have a volume-to-volume content ratio (A)/(B) of 5/95 to 50/50.