50 parts by mass or more of linear low density polyethylene (LLDPE), high pressure polymerization method low density polyethylene (HP-LDPE) and metallocene linear low density polyethylene (m-LLDPE) were blended in a total of less than 50 parts by mass. A porous film containing a resin composition containing 50 to 200 parts by mass of an inorganic filler with respect to 100 parts by mass of a polyethylene resin composition, wherein the heat seal temperature in the machine flow direction (MD) is 90 ° C. or higher, and The porous film is characterized in that the maximum heat seal strength is 4.0 N / 50 mm or more.直鎖状低密度ポリエチレン（ＬＬＤＰＥ）を５０質量部以上、高圧重合法低密度ポリエチレン（ＨＰ－ＬＤＰＥ）とメタロセン系直鎖状低密度ポリエチレン（ｍ－ＬＬＤＰＥ）とを合計５０質量部未満で配合したポリエチレン樹脂組成物１００質量部に対して、無機充填材を５０～２００質量部配合した樹脂組成物を含む多孔質フィルムであって、機械流れ方向（ＭＤ）のヒートシール温度が９０℃以上、かつヒートシール最大強度が４．０Ｎ／５０ｍｍ以上であることを特徴とする多孔質フィルムである。