PROBLEM TO BE SOLVED: To provide absorbent resin particles showing excellence in gel liquid passing velocity and absorption amount under a load.SOLUTION: The absorbent resin particle contains a crosslinked polymer (A) having an acrylic acid (acrylate) and a crosslinking agent (b) as essential components and smectite (B), and is manufactured by a manufacturing method comprising a process of mixing aqueous dispersions of (A) and (B) and/or a process of subjecting the acrylic acid (acrylate) and the crosslinking agent (b) to polymerization reaction in the presence of the aqueous dispersion of (B). The volumetric average particle diameter of the aqueous dispersion of (B) is 10 to 100 nm. The smectite (B) is preferably at least one selected from the group consisting of hectorite, montmorillonite, beidellite, nontronite and saponite. The content of the smectite (B) is preferably 0.01 to 5 wt.% based on the weight of the acrylic acid (acrylate) and the crosslinking agent (b). The absorption amount of the absorbent resin particles under a load is preferably 15 to 27 g/g, and the gel liquid passing velocity is preferably 30 to 250 ml/min.COPYRIGHT: (C)2013,JPO&INPIT【課題】ゲル通液速度及び荷重下吸収量に優れた吸収性樹脂粒子を提供することである。【解決手段】アクリル酸(塩)及び架橋剤(b)を必須構成単位とする架橋重合体(A)と、スメクタイト(B)とを含み、(A)及び(B)の水分散体を混合する工程及び/又は(B)の水分散体の存在下、アクリル酸(塩)及び架橋剤(b)を重合反応させる工程を含む製造方法により製造され、(B)の水分散体積平均粒径が10~100nmであることを特徴とする吸収性樹脂粒子を用いる。スメクタイト(B)はヘクトライト、モンモリロナイト、バイデライト、ノントロナイト及びサポナイトからなる群より選ばれる少なくとも1種が好ましい。スメクタイト(B)の含有量はアクリル酸(塩)及び架橋剤(b)の重量に基づいて0.01~5重量%が好ましい。吸収性樹脂粒子の荷重下吸収量は15~27g/g、またゲル通液速度は30~250ml/分が好ましい。【選択図】なし