An expandable medical balloon includes an inner layer (12) formed of a polymer material having a first flexural modulus of elasticity, an intermediate layer (14) formed of a material having a second flexural modulus of elasticity, a third flexural elasticity And an outer layer (16) formed of a material having a rate. The flexural modulus of the inner and outer layers is from 3,400 atm to about 5,440 atm (50,000 psi to about 80,000 psi, 345 MPa to about 552 MPa), the flexural modulus of the intermediate layer is from about 8,850 atm to about 15,700 atm (About 130,000 psi to about 230,000 psi, about 896 MPa to about 1,586 MPa). The bursting strength of the balloon calculated in a state bent to 90 is not less than about 2,380 atm (about 35,000 psi, about 241 MPa).拡張可能な医療用バルーンは、第一曲げ弾性率を有するポリマー材料で形成された内層(12)と、第二曲げ弾性率を有する材料で形成された中間層(14)と、第三曲げ弾性率を有する材料で形成された外層(16)とを含む。内層及び外層の曲げ弾性率は3,400atm~約5,440atm(50,000psi~約80,000psi、345MPa~約552MPa)であり、中間層の曲げ弾性率は約8,850atm~約15,700atm(約130,000psi~約230,000psi、約896MPa~約1,586MPa)である。90°に屈曲した状態で算出されるバルーンの破裂強度は、約2,380atm(約35,000psi、約241MPa)以上である。