PROBLEM TO BE SOLVED: To provide a method for producing bioactive alumina, in which the surface of an alumina-based substrate is modified so that apatite is formed easily and firmly thereon, and to provide a method for producing an apatite-alumina composite material and the bioactive alumina.SOLUTION: The method for producing bioactive alumina comprises: a substrate formation step ST1 of forming the alumina-based substrate into a predetermined shape a grinding step ST2 of grinding/roughening the surface of the substrate of the predetermined shape and a phosphorus introduction step ST3 of bringing the substrate having the roughened surface into contact with a heated phosphoric acid solution to introduce phosphorus into the roughened surface of the substrate. It does not matter if the substrate having the phosphorus-introduced surface is brought into contact with a calcium ion-containing solution to introduce calcium into the surface of the substrate.【課題】アルミナを主成分とする基材の表面にアパタイトが強固に形成しやすいように改質した生体活性アルミナの製造方法、アパタイト-アルミナ複合材料の製造方法、および生体活性アルミナを提供すること。【解決手段】生体活性を備えた生体活性アルミナを製造するにあたって、基材形成工程ST1において、アルミナを主成分とする所定形状の基材を形成した後、研磨工程ST2において、基材の表面を研磨して基材の表面を粗面にする。次に、リン導入工程ST3では、加熱したリン酸溶液に基材を接触させて基材の表面にリンを導入する。リン導入工程ST3の後、基材とカルシウムイオン含有溶液とを接触させて基材の表面にカルシウムを導入してもよい。【選択図】図1