The present invention relates to a steel artificial fising reef with excellent corrosion resistasnce and growth and development conditions, which includes a blast furnace slag coating layer containing 20-40 wt% of blast furnace slag as a main ingredient, 20-40 wt% of SiO_2, and 10-30 wt% of Al_2O_3 and a steel manufacturing slag coating layer containing 20-40 wt% of FeO, 1-10 wt% of Fe_2O_3, 20-40 wt% of CaO, 5-15 wt% of SiO_2, and 1-10 wt% of Al2O3. The present invention improves corrosion resistance of the artificial fishing reef with the blast furnace slag layer and providses environment suitable for photosynthesis and protein synthesis of marine creatures using cacium and iron contained in the steel manufacturing slag.COPYRIGHT KIPO 2015본 발명은 강재 상기 강재의 표면에 형성되고, 주성분으로 CaO 20-40중량%, SiO2 20-40중량% 및 Al2O3 10-30중량%를 포함하는 고로슬래그 코팅층 및 상기 고로슬래그 코팅층 상부에 형성되고, 주성분으로 FeO 20-40중량%, Fe2O3 1-10중량%, CaO 20-40중량%, SiO2 5-15중량%, 및 Al2O3 1-10중량%를 포함하는 제강슬래그 코팅층을 포함하는 내식성과 생육조건이 우수한 강재어초 및 그 제조방법에 관한 것이다.본 발명에 따르면 고로슬래그 층으로 어초의 내식성을 향상시키고, 제강슬래그에 포함된 칼슘과 철 성분을 이용하여 바다생물들의 광합성과 단백질 합성에 적합한 환경을 제공할 수 있다.