The present invention relates to a method for producing a dental prosthesis based on lithium silicate glass or glass ceramic, the method comprising at least the following method steps: melting a powder mixture containing at least SiO2, Li2O, Al2O3, -Producing spherical, lens-shaped or rod-shaped glass particles solidified from the melt；-separating the glass particles and placing them in a crucible；-melting the glass particles in the crucible； 4 dPa · s <；ν <；80 dPa Adjusting the viscosity s of s, casting the melt thus produced into a female mold corresponding to a dental prosthesis and surrounded by an embedding material, curing the melt in the female mold Crystallization of lithium disilicate from the solidified melt by applying at least one heat treatment step at a temperature of -700 ° C to 900 ° C.本発明は、ケイ酸リチウムガラスまたはガラスセラミックをベースとする歯科補綴物を製造する方法に関し、この方法は少なくとも以下の方法工程・－少なくともＳｉＯ２、Ｌｉ２Ｏ、Ａｌ２Ｏ３を含有する粉末混合物を融解させ、・－溶融物から固化した球形、レンズ形または棒形のガラス粒子を製造し、・－ガラス粒子を分けて、るつぼに入れ、・－るつぼ中のガラス粒子を融解させ、４ｄＰａ・ｓ＜ν＜８０ｄＰａ・ｓの粘度νに調整し、・－こうして製造した溶融物を、歯科補綴物に対応し、埋封材料によって囲まれた雌型中にキャストし、・－溶融物を雌型中で硬化させ、・－７００℃乃至９００℃の温度の少なくとも１つの熱処理工程を加えることによって、固化した溶融物から二ケイ酸リチウムを結晶化させることを含む。