Provided are dental articles, and methods of making articles, having an aesthetic inorganic coating based on zirconia at least partially stabilized with yttrium oxide, calcium oxide, cerium oxide, or magnesium oxide. Stabilized zirconia coatings were found to provide a smooth, low friction surface having high abrasion resistance. These coatings are particularly applicable to orthodontic appliances. While virgin stabilized zirconia coatings can often have an undesirable color cast, it was discovered that this color cast can be substantially eliminated by heat treating the coated appliance in an oxygenated environment. The combination of depositing a stabilized zirconia coating and subsequently heat treating to decolorize the coating provides a surprisingly robust, stable, low-friction coating that is also aesthetic.酸化イットリウム、酸化カルシウム、酸化セリウム、又は酸化マグネシウムによって少なくとも部分的に安定化されたジルコニアに基づく美的な無機コーティングを有する歯科用物品及び、歯科用物品の作製方法が提供される。安定化されたジルコニアコーティングは高い耐摩耗性を有する滑らかな低摩擦表面を提供することが見出された。これらのコーティングは歯列矯正装置に特に適用可能である。新しい安定化ジルコニアコーティングは不要な色かぶりをしばしば有する場合があるが、コーティングされた装置を酸素化環境において熱処理することによってこの色かぶりを実質的に除去できることが発見された。安定化ジルコニアコーティングの蒸着と、その後の、コーティングの脱色のための熱処理とを組合せることは、驚くほど堅牢で安定かつ低摩擦な上、美的でもあるコーティングを提供する。【選択図】図2