Disclosed in the invention is a preparation method of an antibacterial cornea repair material, including the following steps: (1) purifying type Ι collagen extracted from beef tendons, and using an acetic acid or hydrochloric acid solution to prepare a collagen solution with a concentration of 6.0-10.0 mg/ml (2) casting the collagen solution into the forming mould of the cornea repair material, and then naturally air drying at room temperature to form a membrane (3) soaking the obtained collagen membrane in an antibiotic solution, stirring until the membrane is fully in contact with the solution and then adding a crosslinking agent and a catalyst to the above-mentioned solution, and stirring to perform a crosslinking reaction and (4) taking out the crosslinked membrane material obtained in step (3) and washing 3-5 times with deionized water, and then naturally air drying at room temperature to obtain the antibacterial cornea repair material. The material has relatively good mechanical properties, optical properties and biocompatibility, and has a good antibacterial effect. It can be used for repairing and replacing damaged cornea tissue in the field of medicine.La présente invention concerne une méthode de préparation dun tissu antibactérien de réparation de la cornée comprenant les étapes suivantes consistant à : (1) purifier du collagène de type I extrait de tendons de bœuf et utiliser une solution dacide acétique ou dacide chlorhydrique pour préparer une solution de collagène ayant une concentration de 6,0 à 10,0 mg/mL (2) couler la solution de collagène dans le moule de formation du tissu de réparation de la cornée, et ensuite laisser sécher naturellement à lair à température ambiante pour former une membrane (3) tremper la membrane en collagène obtenue dans une solution antibiotique, agiter jusquà ce que la membrane soit totalement en contact avec la solution et ajouter ensuite un agent de réticulation et un catalyseur à la solution mentionnée ci-dessus, pui