The present invention relates to a nano-oxygen catalyst for removing sick house syndrome. The nano-oxygen catalyst is prepared by mixing 0.23-0.35 mol of nitric acid in a titanium dioxide for primary stirring, mixing 0.12-0.25 mol of silica for secondary stirring, 0.013-0.03 mol of acryl binders for tertiary stirring, and adding a dispersing agent and EDTA for quarternary stirring, thereby easily and completely removing volatile organic compounds (VOC) such as formaldehyde, toluene, xylene, and benzene which are typical materials causing sick house syndrome by being simply applied on the surface of an interior finishing material. Therefore, as a test report describes, the nano-oxygen catalyst removes the smell of 48 umol/mol of formaldehyde to 89.6% within 120 minutes and is capable of semipermanent use without the reduction of the effect as a catalyst type which does not respond to VOC or other pollutants.본 발명은 새집증후군 제거용 나노산소 촉매제에 관한 것으로, 이산화티탄 용액에 질산 0.23 내지 0.35 mol을 혼합 1차 교반하고, 실리카 0.12 내지 0.25 mol을 혼합 2차 교반하고, 아크릴 바인더 0.013 내지 0.03 mol을 혼합 3차 교반하고, 분산제 및 EDTA를 첨가한 후 4차 교반하여 제조됨으로써, 새집증후군의 대표물질인 포름알데히드, 톨루엔, 자일렌 및 벤젠 등과 같은 휘발성 유기화합물(VOC)을 실내 마감재 표면에 간단한 도포를 통해 용이하고 확실하게 제거할 수 있는 바, 이는 시험성적서에 명기된 바와 같이 120분 이내에 48 μmol/mol의 농도의 포름알데히드를 89.6% 까지 탈취할 수 있음은 물론, 휘발성 유기화합물이나 기타 오염물질과는 반응하지 않는 촉매 타입으로써 반영구적으로 효능이 저하되지 않고 사용할 수 있는 효과가 있다.