FIELD: medicine.SUBSTANCE: invention relates to medicine, specifically to ceramic and cement materials, and discloses a method for producing calcium carbonate-based biocement for filling bone defects. Method is characterized by that the cement grout is obtained by successively adding an additive to the suspension, then the suspension and additives are mixed for 0.5-1 minutes, then calcium carbonate powder is added to the resulting mixture with constant stirring for 1-2 minutes until a uniform cement grout is obtained with a specially selected ratio of components. Resulting cement grout takes 3-8 minutes to form a cement stone, it consists of crystalline phases - calcite and dicalcium phosphate, as well as amorphous calcium phosphate obtained cement stone is characterized by porosity of 40-70%, a pore size of 500-2,000 μm, and strength of at least 4 MPa.EFFECT: invention can be used for plastic reconstruction of damaged bone tissue.1 cl, 1 tbl, 1 exИзобретение относится к области медицины, а именно к керамическим и цементным материалам, и раскрывает способ получения биоцемента на основе карбоната кальция для заполнения костных дефектов. Способ характеризуется тем, что цементный раствор получают в результате последовательного добавления в суспензию добавки, затем проводят смешение суспензии и добавки в течение 0,5-1 мин, затем в полученную смесь добавляют порошок карбоната кальция при постоянном перемешивании в течение 1-2 мин до получения однородного цементного раствора при специально подобранном соотношении компонентов. Полученный цементный раствор схватывается в течение 3-8 мин с образованием цементного камня, состоящего из кристаллических фаз - кальцита и дикальцийфосфата, а также аморфного фосфата кальция полученный цементный камень характеризуется пористостью 40-70%, размером пор 500-2000 мкм, прочностью не менее 4 МПа. Изобретение может быть использовано для пластической реконструкции поврежденных костных тканей. 1 табл., 1 пр.