Provided is a zirconia sintered body with improved strength between the layers of laminated powder. Multiple zirconia powders are formed having different compositions and containing zirconia and a stabilizer for suppressing phase shifts of the zirconia, a zirconia composition is formed by laminating the multiple zirconia powders, and a zirconia sintered body is produced by sintering the zirconia composition, the bending strength thereof being 1100MP or greater, measured in conformity with JISR 1601 on a sintered body test piece in which the boundaries of the multiple zirconia powders traverse the test piece along the load applying direction, the load points being aligned with the boundary positions in the three-point bending test.L'invention fournit un corps fritté de zircone dont la résistance entre des couches de poudres stratifiées est élevée. Selon l'invention, une pluralité de poudres de zircone de compositions différentes, et comprenant une zircone et un agent stabilisant inhibant les transitions de phase de la zircone, est formée, une composition de zircone est formée par stratification de la pluralité de poudres de zircone, et un corps fritté de zircone dans lequel la composition de zircone est frittée, est fabriqué. La résistance à la flexion mesurant, conformément à JISR1601 et selon la position d'interfaces, le point de charge d'un essai de flexion en trois points, sur un échantillon du corps fritté dans lequel les interfaces entre la pluralité de poudres de zircone, sont présentes de manière à traverser l'échantillon dans une direction d'application de charge, est supérieure à 1100MPa.粉末を積層した層間の強度を高めたジルコニア焼結体を提供する。ジルコニア及びジルコニアの相転移を抑制する安定化剤を含有し、組成が異なる複数のジルコニア粉末を形成し、複数のジルコニア粉末を積層させてジルコニア組成物を形成し、ジルコニア組成物を焼結させたジルコニア焼結体を作製し、ＪＩＳＲ１６０１に準拠し、複数のジルコニア粉末の境界が荷重印加方向に沿って試験片を横断するように存在する焼結体の試験片に対して、３点曲げ試験の荷重点を境界の位置に合わせて測定した曲げ強度が１１００ＭＰａ以上である。