The method for producing an elastic laminate according to the present invention comprises the step of co-extruding a first web (F) comprising an elastic film comprising at least three layers (F1, F2, F1) having at least two different polymer materials； Sending the co-extruded first elastic film web (F) and the two second nonwoven webs (T1, T2) simultaneously to a heat-bonded calendar, where the first elasticity when entering the calendar (14) When the film web (F) is disposed between the two second nonwoven webs (T1, T2) and during the operation from the co-extrusion process to the heat bonding process, the first elastic film web (F) A process of shifting from a molten state in the co-extrusion process to a solidified and cooled state when entering the calendar (14), spot welding or area welding in the calendar (14) ( ) To bond the second nonwoven web (T1, T2) to each opposing outer layer of the first elastic film web (F) to produce an intermediate web (P1) and across the web A step of mechanically extending the intermediate web (P1) in a direction is provided in the same production line. [Selection] Figure 1本発明に係る弾性積層体の製造方法は、少なくとも二つの異なるポリマー材料を有する少なくとも三つの層（Ｆ１，Ｆ２，Ｆ１）を備えた弾性フィルムから成る第一ウェブ（Ｆ）を共押出しする工程、前記共押出した第一弾性フィルムウェブ（Ｆ）と、二つの第二不織布ウェブ（Ｔ１，Ｔ２）とを同時に熱結合カレンダに送る工程であって、そこで、カレンダ（１４）に入る時に第一弾性フィルムウェブ（Ｆ）が前記二つの第二不織布ウェブ（Ｔ１，Ｔ２）の間に配置され、かつ、共押出し工程から熱結合工程への動作中に、前記第一弾性フィルムウェブ（Ｆ）が、共押出し工程における溶融状態から、カレンダ（１４）に入る時に固化及び冷却状態に移行するようにされる工程、前記カレンダ（１４）におけるスポット溶接又は領域溶接（Ｚ）を通して、前記第二不織布ウェブ（Ｔ１，Ｔ２）を、前記第一弾性フィルムウェブ（Ｆ）の各対向する外側層に結合して、中間ウェブ（Ｐ１）を製造する工程、及び同ウェブを横切る方向に前記中間ウェブ（Ｐ１）を機械的に伸長させる工程を同じ製造ラインで備えていることを特徴とする。【選択図】図１