The invention discloses a blank for producing dental shaped parts which consists entirely of porous glass without crystalline portions. The density of the blank is between 50% and 95% of its theoretical density. It has a discoidal shape with a diameter of at least 20 mm. The blank is produced by a process in which glass powder is first pressed at a pressure of between 10 MPa and 300 MPa and this green body is (pre-)sintered at a temperature of between 580° C. and 750° C. to form a blank of porous glass without crystalline portions. From the obtained blank, monolithic dental shaped parts can be obtained by mechanical processing followed by sintering, wherein a process according to the invention for stabilizing the shape of the shaped parts is used.본 발명은 결정질 물질 없이 전적으로 다공질 유리로 이루어진 치과용 성형 부품을 제조하기 위한 블랭크에 관한 것이다. 블랭크의 밀도는 그의 이론상 밀도의 50% 내지 95% 범위이다. 이는 직경이 20 mm 이상인 디스크 유사 형상을 갖는다. 블랭크는 유리 분말을 먼저 10 MPa 내지 300 MPa 범위의 압력에서 가압하고 당해 생소지를 580℃ 내지 750℃ 범위의 온도에서 (예비)소결시켜 결정질 물질 없이 다공질 유리로 이루어진 블랭크를 수득하는 방법에 의해 제조된다. 일체식 치과용 성형 부품은 생성된 블랭크로부터 기계적 기계처리 및 후속 소결에 의해 될 수 있고, 여기서 본 발명의 따른 방법을 이용하여 성형 부품의 형상을 안정화시킨다. 유리는 바람직하게는 SiO2 50 내지 80 중량%, Al2O3 3 내지 24 중량%, K2O 3 내지 13 중량%, Na2O 3 내지 13 중량%, Li2O 0 내지 4 중량%, B2O3 0 내지 4 중량%, F 0 내지 4 중량%, TiO2 0 내지 8 중량%, ZrO2 0 내지 8 중량%, P2O5 0 내지 4 중량%, SnO2 0 내지 4 중량%, MgO 0 내지 4 중량%, CaO 0 내지 4중량%, BaO 0 내지 4중량%, Sb2O3 0 내지 4중량%, CeO2 0 내지 8중량%를 함유한다.