The present invention relates to an inorganic material comprising particles of three-dimensional ordered macroporous structure comprising spherical pores, - said pores having an average pore diameter ranging from 50 nm to 10 µm, - the pore diameter varying by no greater than 20%, - the surface of said pores being coated by an absorber agent of the visible wavelength spectrum, - said particles having an average largest dimension ranging from 1 to 50 µm, and wherein - said particles are coated with at least a hydrophobic component. The invention further relates to a process for preparing said inorganic material.La présente invention concerne un matériau inorganique comprenant des particules de structure macroporeuse ordonnée tridimensionnelle comprenant des pores sphériques, - lesdits pores ayant un diamètre de pore moyen allant de 50 nm à 10 µm, - le diamètre de pore variant de 20 % au maximum, - la surface desdits pores étant revêtue dun agent dabsorption du spectre de longueur donde visible, - lesdites particules ayant une dimension maximale moyenne allant de 1 à 50 µm, et - lesdites particules étant revêtues dau moins un constituant hydrophobe. La présente invention concerne en outre un procédé pour préparer ledit matériau inorganique.