The invention relates to cross-linked sodium hyaluronate gel for tissue filler for plastic surgery and a preparation method thereof. The gel is prepared by enabling sodium hyaluronate alkaline solution, epoxy group containing long-chain alkane and epoxy group containing cross-linking agent to react for 2-5 hours at 35-50°C, then washing, gelling and sterilizing, wherein the molar ratio of the sodium hyaluronate alkaline solution, the epoxy group containing cross-linking agent to the epoxy group containing long-chain alkane is 10:4-1:1-4, and the number of carbon atoms of the epoxy group containing long-chain alkane is 6-18. The gel according to the invention has the advantages that on one hand, enzymolysis resistance can be effectively improved, and the gel is more stable and on the other hand, the excellent intrinsic biocompatibility of the sodium hyaluronate can be maintained, and injectability is unaffected.Linvention concerne un gel dhyaluronate de sodium réticulé destiné à un matériau de comblement tissulaire pour la chirurgie plastique et son procédé de préparation. On prépare le gel en permettant la réaction dune solution alcaline dhyaluronate de sodium, dun alcane à longue chaîne contenant un groupe époxy et dun agent de réticulation contenant un groupe époxy pendant 2-5 heures à 35-50°C puis en lavant, gélifiant et stérilisant. Selon linvention, le rapport molaire de la solution alcaline dhyaluronate de sodium, de lagent de réticulation contenant un groupe époxy à lalcane à longue chaîne contenant un groupe époxy vaut 10:4-1:1-4, et le nombre datomes de carbone de lalcane à longue chaîne contenant un groupe époxy vaut 6-18. Le gel selon linvention présente les avantages selon lesquels, dune part, la résistance à lenzymolyse peut être améliorée de manière efficace et le gel est plus stable et dautre part, lexcellente biocompatibilité intrinsèque de lhyaluronate de sodium peut être conservée et laptitude à linjection nest pas affectée.