PROBLEM TO BE SOLVED: To provide a glass for a medicine container and a glass tube using the same, enabling sufficient chemical strengthening of the container after forming into final products such as an ampule, a vial, a pre-filled syringe and a cartridge.SOLUTION: A glass for chemical strengthening contains a composition containing, by mol%, SiO2:50 to 80%, Al2O3:5 to 30%, Li2O:0 to 2%, Na2O:5 to 25%. A glass tube is formed by a Danner process and applied to a chemical strengthening treatment by an ion exchange treatment in a molten salt. A glass for a medicine container has a compressive stress value of a compressive stress layer formed at the ion exchange treatment in KNO3 molten salt at 440°C of 300 MPa or more, and a thickness of the compressive stress layer of 10 μm or more, and a heat expansion coefficient in the temperature range of 30 to 380°C of 100×10-7/°C or less.COPYRIGHT: (C)2014,JPO&INPIT【課題】アンプル、バイアル、プレフィルドシリンジ、カートリッジなどの最終製品に成形した後に、容器を十分に化学強化できる、医薬品容器用ガラス及びこれを用いたガラス管を提供する。【解決手段】モル%で、SiO2 50~80%、Al2O3 5~30%、Li2O 0~2%、Na2O 5~25%含有することを特徴とする組成の学強化用ガラス。ガラス管はダンナー法で成形され、溶融塩中でイオン交換処理されて化学強化処理される。440℃のKNO3溶融塩中でイオン交換処理を行った際に形成される圧縮応力層の圧縮応力値が300MPa以上、且つ圧縮応力層の厚みが10μm以上であり、30~380℃の温度範囲における熱膨張係数が100×10-7/℃以下である医薬品容器用ガラス。【選択図】なし