[Means for solution] A dental curable composition has a curing time of 30 seconds to 120 minutes and includes a compound having an acidic group in the molecule (A), a polymerizable monomer (B), an organic amine compound (C) and a sulfur-containing reducing compound (D). In the dental curable composition, the content of the component (A) is 0.01 to 80 parts by weight, the content of the component (B) is 21 to 99.8 parts by weight, the content of the component (C) is 0.01 to 30 parts by weight and the content of the component (D) is 0 to 30 parts by weight (the total of the components (A) to (D) is 100 parts by weight. When any of the compounds belongs to a plurality of the components (A) to (D), the parts by weight of the compound is divided by the number of the components to which the compound belongs, and the quotient is used as the content of each component). [Advantage] The composition may be cured at a relatively low temperature close to the body temperature without using a peroxide-based polymerization initiator, and has good sealing property and adhesion.본 발명의 치과용 경화성 조성물은 경화 시간이 30초∼120분의 치과용 경화성 조성물이며, 그 치과용 경화성 조성물이 (A) 분자 내에 산성기를 갖는 화합물, (B) 중합성 단량체, (C) 유기 아민 화합물 및 (D) 황 함유 환원 화합물을 함유하고, 그 치과용 경화성 조성물 중에서의 (A) 성분 함유량이 0.01∼80중량부, (B) 성분 함유량이 21∼99.8중량부, (C) 성분 함유량이 0.01∼30중량부, (D) 성분 함유량이 0∼30중량부의 양으로 함유되어 있는 것을 특징으로 하는 치과용 경화성 조성물(단, 상기 (A)∼(D) 성분의 합계를 100중량부로 한다. 또한 상기 (A)∼(D)의 복수에 해당하는 화합물이 존재할 경우에는 그 화합물의 중량부를 해당하는 성분수로 나눈 중량부를 해당하는 성분마다의 함유량으로 한다).본 발명에 의하면, 과산화물계의 중합 개시제를 사용하지 않고, 체온 부근의 비교적 저온 영역에서, 조성물을 경화시킬 수 있고, 씰링성, 접착성도 양호하다.