The present invention provides a zirconia sintered body comprising a fluorescent agent and excellent light transmittance and strength, a zirconia molded body obtained from the zirconia sintered body, and a zirconia plastic body. The present invention is a zirconia sintered body containing a fluorescent agent, comprising yttria 4.5 to 9.0 mol%, a crystal grain diameter of 180 nm or less, and a zirconia sintered body having a three-point bending strength of 500 MPa or more； A zirconia molded body containing a fluorescent agent, containing 4.5 to 9.0 mol% of yttria, a three-point bending strength after sintering at 1100 ° C for 2 hours under normal pressure and 500 MPa or more, and crystal grain size after sintering at 1100 ° C for 2 hours under normal pressure. A zirconia molded body having a thickness of 180 nm or less； A zirconia plasticizer containing a fluorescent agent, containing 4.5 to 9.0 mol% of yttria, a three-point bending strength after sintering at 1100 ° C for 2 hours under normal pressure and 500 MPa or more, and crystallization after sintering for 2 hours at 1100 ° C under normal pressure. It relates to a zirconia plastic body having a particle diameter of 180 nm or less.본 발명은, 형광제를 포함하고, 투광성과 강도가 우수한 지르코니아 소결체, 그 지르코니아 소결체가 얻어지는 지르코니아 성형체 및 지르코니아 가소체를 제공한다. 본 발명은, 형광제를 포함하는 지르코니아 소결체로서, 이트리아를 4.5 ∼ 9.0 몰％ 포함하고, 결정 입경이 180 ㎚ 이하이고, 3 점 굽힘 세기가 500 ㎫ 이상인 지르코니아 소결체 ； 형광제를 포함하는 지르코니아 성형체로서, 이트리아를 4.5 ∼ 9.0 몰％ 포함하고, 상압하 1100 ℃ 에서 2 시간 소결 후의 3 점 굽힘 세기가 500 ㎫ 이상이고, 상압하 1100 ℃ 에서 2 시간 소결 후의 결정 입경이 180 ㎚ 이하인 지르코니아 성형체 ； 형광제를 포함하는 지르코니아 가소체로서, 이트리아를 4.5 ∼ 9.0 몰％ 포함하고, 상압하 1100 ℃ 에서 2 시간 소결 후의 3 점 굽힘 세기가 500 ㎫ 이상이고, 상압하 1100 ℃ 에서 2 시간 소결 후의 결정 입경이 180 ㎚ 이하인 지르코니아 가소체에 관한 것이다.