Process for the preparation of a particulate dental filler composition, comprising the following steps: (a) introducing a mixture containing (a1) a silica precursor component, and (a2) a solution or dispersion of one or more compounds selected from compounds of aluminum, zinc, titanium, zirconium, tungsten, ytterbium, hafnium, bismuth, barium, strontium, silver, tantalum, lanthanum, tin, boron, and cerium, into a pulsed reactor； (b) converting the silica precursor component and the compounds into a particulate mixed oxide with a pulsed gas flow resulting from flameless combustion； (c) isolating the particulate mixed oxide from the pulsed reactor； (d) optionally subjecting the particulate mixed oxide to a heat treatment step； and (e) treating the optionally heat-treated particulate mixed oxide with a silane treatment agent for obtaining a particulate dental filler composition.La présente invention concerne un procédé pour la préparation d'une composition de charge dentaire particulaire, comprenant les étapes suivantes consistant à : (a) introduire dans un réacteur pulsé un mélange contenant (a1) un constituant précurseur de silice, et (a2) une solution ou une dispersion d'un ou de plusieurs composés choisis parmi des composés d'aluminium, de zinc, de titane, de zirconium, de tungstène, d'ytterbium, de hafnium, de bismuth, de baryum, de strontium, d'argent, de tantale, de lanthane, d'étain, de bore, et de cérium ； (b) convertir le constituant précurseur de silice et les composés en un oxyde mixte particulaire avec un flux de gaz pulsé résultant d'une combustion sans flamme ； c) isoler l'oxyde mixte particulaire du réacteur pulsé ； (d) soumettre éventuellement l'oxyde mixte particulaire à une étape de traitement thermique ； et e) traiter l'oxyde mixte particulaire, éventuellement traité thermiquement, avec un agent de traitement silane pour obtenir une composition de charge dentaire particulaire.