The present invention provides a silicate glass capable of suppressing a change in color tone of a zirconia as a base material and a dental product using the same, even when firing at the same time as the zirconia microparticles. In the present invention, 65.0 to 90.0 mol% of SiO 2 , 4.0 to 15.0 mol% of Al 2 O 3 , 1.0 to 10.0 mol% of K 2 O, 0.1 to 7.0 mol% of Na 2 O, and 0.01 to 15.0 mol of % Of CaO, substantially no B 2 O 3 , {(molar number of Al 2 O 3 )/(total molar number of RO + R 2 O)} is 0.70 or more, and the metal oxide represented by RO A silicate glass in which R represents a metal element of group 2 or 12 of the periodic table, and R of the metal oxide represented by R 2 O represents a metal element of group 1 of the periodic table； A composite comprising a substrate composed of the silicate glass and ceramics: a sintered body obtained by firing the composite； And a dental product comprising the sintered body.본 발명은, 지르코니아 미소결체와 동시에 소성해도, 기재인 지르코니아의 색조의 변화를 억제할 수 있는, 실리케이트 유리, 및 이것을 사용한 치과용 제품을 제공한다. 본 발명은, 65.0 ∼ 90.0 mol％ 의 SiO2, 4.0 ∼ 15.0 mol％ 의 Al2O3, 1.0 ∼ 10.0 mol％ 의 K2O, 0.1 ∼ 7.0 mol％ 의 Na2O, 및, 0.01 ∼ 15.0 mol％ 의 CaO 를 함유하고, B2O3 을 실질적으로 함유하지 않고, {(Al2O3 의 몰수)/(RO ＋ R2O 의 합계 몰수)} 가 0.70 이상이고, 상기 RO 로 나타내는 금속 산화물의 R 은 주기표의 제 2 족 또는 제 12 족의 금속 원소를 나타내고, R2O 로 나타내는 금속 산화물의 R 은 주기표의 제 1 족의 금속 원소를 나타내는, 실리케이트 유리 ； 당해 실리케이트 유리와 세라믹스로 이루어지는 기재를 포함하는 복합체 : 그 복합체를 소성하여 이루어지는 소결체 ； 및, 당해 소결체로 이루어지는 치과용 제품에 관한 것이다.