The present invention relates to a process for the production of water-absorbing polymer structures, comprising the process steps of providing of an aqueous monomer solution comprising a polymerizable, monoethylenically unsaturated monomer (&alpha；1) carrying acid groups or a salt thereof； free-radical polymerization of the aqueous monomer solution to give a polymer gel, drying of the optionally comminuted polymer gel to give water-absorbing polymer structures, and surface post-crosslinking of the optionally ground and sieved water-absorbing polymer structures, wherein a thermoplastic polymer is added to the aqueous monomer solution before process step ii) or during process step ii), preferably before process step ii), or II) the polymer gel after process step ii) and before process step iv) or during process step iv), preferably before process step iv), or III) the water-absorbing polymer structure after process step iv).본 발명은 수분-흡수성 중합체 구조를 제조하기 위한 방법에 관한 것으로, 상기 방법은,ⅰ) - 산성기 또는 그 염을 포함하는 중합성, 모노에틸렌계 불포화 단량체(α1)- 상기 단량체(α1)와 중합될 수 있는 선택적인 모노에텔렌계 불포화 단랑체(α2), 및- 선택적인 가교제(α3)를 포함하는 수성 단량체 용액을 제공하는 단계,ⅱ) 중화체 겔을 얻도록 상기 수성 단량체 용액을 라디칼 중합하는 단계,ⅲ) 상기 중합체 겔을 선택적으로 분쇄하는 단계,ⅳ) 수분-흡수성 중합체 구조를 얻도록 상기 선택적으로 분쇄한 중합체 겔을 건조시키는 단계,ⅴ) 상기 수분-흡수성 중량체 구조를 선택적으로 연삭(grinding) 및 체질(sieving)하는 단계 및ⅵ) 상기 선택적으로 연삭 및 체질한 수분-흡수성 중량체 구조를 표면 후-가교하는 단계를 포함하며,여기서 열가소성 중합체는Ⅰ) 제조 단계 ⅱ)의 전 또는 제조 단계 ⅱ) 동안, 바람직하게는 제조 단계 ⅱ)의 전의 상기 수성 단량체 용액,Ⅱ) 제조 단계 ⅱ)의 후 및 제조 단계 ⅳ)의 전, 또는 제조 단계ⅳ)의 동안, 바람직하게는 제조 단계 ⅳ)의 전의 상기 중합체 겔, 또는Ⅲ) 제조 단계 ⅳ)의 후의 상기 수분-흡수성 중량체 구조에 첨가된다.본 발명은 또한 상기 방법에 의해 얻을 수 있는 수분-흡수성 중합체 구조, 수분-흡수성 중합체 구조, 조성물질, 조성물질의 제조방법, 상기 방법에 의해 얻을 수 있는 조성물질, 폼(foam), 성형품(shaped articles), 섬유(fibres), 포일(foils), 필름(films), 케이블(cables), 실링제(sealing materials), 액체-흡수 위생 용품(liquid-absorbing hygiene articles), 식물 및 진균 성장-조절제용 캐리어(carriers for plant and fungal growth-regulating agents), 포장재(packaging material), 토양 첨가제(soil additives) 또는 건축자재(building materials)와 같은 화학 제품, 수분-흡수성 중합체 구조의 용도 및 열가소성 중합체의 용도에 관한 것이다.