A preparation method of homopolymerized N-vinyl butyl lactam iodine with an effective iodide content of 20%, comprises: using an N-vinyl butyl lactam iodine homopolymer and iodine with the particle size being small than 850 μm as raw materials, the mass ratio of the N-vinyl butyl lactam iodine homopolymer to the iodine with the particle size being small than 850 μm being 7:3-5:5 meanwhile, with the amount of the raw materials being the reference, adding an additive of 0.01%-5% by weight stirring at the temperature of 50-100°C for reaction for 5-20 hours in a segmented preparation manner. The additive may be sodium citrate, sodium chloride, or sodium acetate.La présente invention concerne un procédé de préparation diode de N-vinyl butyl lactame homopolymérisé ayant une teneur effective en iode de 20 %, consistant à : utiliser un homopolymère diode de N-vinyl butyl lactame et de liode dont les particules ont une taille inférieure à 850 μm comme matières premières, le rapport de masse entre lhomopolymère diode de N-vinyl butyl lactame et liode dont les particules ont une taille inférieure à 850 μm allant de 7/3 à 5/5 dans le même temps, en utilisant la quantité de matières premières comme référence, ajouter un additif de 0,01 % à 5 % en poids agiter à une température allant de 50 à 100 °C pour que la réaction se produise pendant 5 à 20 heures, selon une manière de préparation segmentée. Ladditif peut être du citrate de sodium, du chlorure de sodium ou de lacétate de sodium.