PROBLEM TO BE SOLVED: To provide a production process of a pet urinal pad having a deammoniation function and a high saline water absorption ability.SOLUTION: A production process of a pet urinal pad having a deammoniation function and a high saline water absorption ability comprises: (A) milling and sieving natural zeolites to obtain zeolite powder having a particle size of smaller than 100 microns (B) immersing the zeolite powder into 1 mol/L sulfuric acid for processing for 10-60 minutes under a processing temperature of 50-80 degrees centigrade performing vacuum filtration and drying on the processed zeolite powder to obtain zeolite oxides (C) adding 2-10 pts.mass of zeolite oxides into 100 pts.mass of superabsorbent resin, and thoroughly and uniformly mixing them to obtain a mixture (D) fitting the mixture formed in step (C) with pulp paper to form a deodorization water absorption layer and (E) covering a PE film and a nonwoven fabric on the deodorization water absorption layer to form the pet urinal pad having the deammoniation function and the high saline water absorption ability.SELECTED DRAWING: NoneCOPYRIGHT: (C)2016,JPO&INPIT【課題】脱アンモニア機能及び高い塩水吸収能力のあるペット用尿パッドの製造プロセスを提供する。【解決手段】脱アンモニア機能及び高い塩水吸収能力のあるペット用尿パッドの製造プロセスは、天然沸石を細かく磨き、篩にかけることで、粒径が100ミクロン未満となる沸石粉を得る手順Aと、沸石粉を濃度1mol/Lの硫酸処理に10~60分の時間で浸入し、処理温度が50~80摂氏度とし、処理された沸石粉を真空で吸収濾過して乾燥させることで、酸化沸石を得る手順Bと、100質量部の高吸水性樹脂に2~10質量部の酸化沸石を入れ、充分に均一に混合することで混合物を得る手順Cと、前記手順Cで形成された混合物をパルプ紙に密接することで脱臭吸水層を形成する手順Dと、脱臭吸水層上にPE膜(素地)及び不織布(表面被覆層)を被覆することで、脱アンモニア機能及び高い塩水吸収能力を備えるペット用尿パッドを形成する手順Eと、を含む。【選択図】なし