Elastin-like polymers (ELP) are shown to demonstrate dynamic behavior atop silica, simillar to visco-elastic polymer dewetting. A combination of multiple factors are shown to contribute to this behavior including the hydrophilicity of the silica preventing the adsorption of ELP, the formation of a salt layer between ELP and silica, and the ability of the silica and salt layer to hold on to minute amounts of water for prolonged periods. Further, the addition of a polyethyleneimine (PEI) block to the terminal end of ELP allows the particle radius as well as LCST to be controlled by changing any combination of polymer concentration, NaCl concentration, and pH. The addition of the PEI block also provides the ability to crosslink the copolymers and achieve a stable particle radius after formation in harsh environments.On a montré que les polymères de type élastine (ELP) présentent un comportement dynamique supérieur à celui de la silice, similaire au démouillage de polymères viscoélastiques. On a montré qu'une combinaison de facteurs multiples contribue à ce comportement, comprenant l'hydrophilie de la silice empêchant l'adsorption des ELP, la formation d'une couche de sel entre les ELP et la silice et l'aptitude de la couche de silice et de sel à tenir sur des quantités minuscules d'eau pendant des périodes prolongées. En outre, l'ajout d'un bloc de polyéthylène-imine (PEI) à l'extrémité terminale des ELP permet de réguler le rayon de particule ainsi que la LCST par modification d'une quelconque combinaison de concentration en polymère, de concentration en NaCl et de pH. L'ajout du bloc de PEI permet également de réticuler les copolymères et d'obtenir un rayon de particule stable après la formation dans des environnements hostiles.